Carbon prepreg C210T2pp

MECHANICAL PROPERTIES OF LAMINATE
Cured at 130 oC for 60 minutes and 3 bar
Flexural strength (Mpa): 850
Flexural modulus (Gpa): 54
Tensile strength (MPa): 550
Tensile modulus (GPa): 60
ILSS - Short Beam Shear (Mpa): 67
Tg (DSC) 20 oC / min: 128 oC

 Carbon sleeve
CSL60

Linear weight: 34.52 g / m
Warp: 3K carbon fiber, 50%
Weft: 3K carbon fiber, 50%

Length, diameter and linear weight of braids vary greatly, depending on tension (stretch) applied. Technical data and price are given to the point where warp and weft are at the +- 45 degree angle (or vertical to each other).

Carbon aramid fabric
CK210T2

Areal weight: 210 g / m2
Weaving style: Twill 2X2
Width: 1.20 meters
Warp: 3K TR30S carbon fiber + aram. 1260, 50%, 3.2+3.2=6,4 ends(threads) / cm
Weft: 3K TR30S carbon fiber + aram. 1260, 50%, 3.2+3.2=6,4 ends(threads) / cm
Fiber content by weight: 61% carbon / 39% aramid

MECHANICAL PROPERTIES OF FIBERS USED
Carbon:
Tensile strength (MPa): 4410
Tensile modulus (GPa): 235
Elongation at break (%): 1.9
Aramid:
Tensile strength (MPa): 2987
Tensile modulus (GPa): 91
Elongation at break (%): 3.10